In the Advanced zinc alloy for casting plastic mold factory , because of its poor mechanical properties , can only be used in 

the manufacture of plastic mold processing or experimental small batch production of plastic mold. In many cases, they are

 more subject to high mechanical loads for the manufacture of plastic blow molding or vacuum forming mold . And copper 

alloys , zinc alloys having a high heat conductivity , the heat rate of the home 105w / (mk)

Zinc alloy die casting process made ​​by the majority , which is characterized by fever casting temperature

 ( melting point of 390 degrees , burning casting temperature 410-450 degrees) low. Thus , in addition to steel , wood models

 are available , plaster , plastic or even to produce . Plaster and plastic model making up that easy and quick. Zinc alloy can

 be cast in the same mold of sand and cement mold. Casting, despite possible but rarely used. In the casting process , 

the zinc alloy is an excellent characteristic shape of the complex structures can be formed of a smooth non-porous surface .

 Before casting for models , especially the cast must be fully dry. ( Gypsum dried at 220 degrees for a few days ) , otherwise

 the benefits of the casting to form a porous and vapor焅coarse surface .

The same can be advanced zinc alloy die cold extrusion molding, extrusion blanks before preheated to 200 to 250 degrees,

 even though this process is a deep cavity is also just one step without intermediate annealing . Cold pressing the male die

 used to have the hardness HB430 . Cold extrusion process, sometimes accompanied by a rotational movement of the 

vertical motion , cavity inserts such as helical gears can be manufactured with this male mold .

Another method for processing high grade zinc alloy coating is a metal mold .

High mechanical strength due to the lower zinc alloy , it can only be used to make the cavity inserts , and these inserts mounted

 to a steel mold , the steel mold in the molding process used to withstand the clamping force and injection pressure .

In the plastic mold factory, zinc alloy used to make the most suitable cavity inserts.